Density                       2.77 g/cm3 (173 lb/ft3)Elastic (Young's, Tensile) Modulus   73 GPa (11 x 106 psi)Electrical Conductivity                     30 % IACSElongation at Break                             5 %Melting Onset (Solidus)               502 °C (940 °F)Shear Modulus                  28 GPa (4.1 106 psi)Specific Heat Capacity                     870 J/kg-KDefinition of Specific Heat Capacity Strength to Weight Ratio                 173 kN-m/kgTensile Strength: Ultimate (UTS)       480 MPa (70 x 103 psi)Tensile Strength: Yield (Proof)        360 MPa (52 x 103 psi)Thermal Conductivity                     120 W/m-KThermal Diffusivity                        50Thermal Expansion                      22.8 µm/m-KAlloy CompositionAluminum (Al)                       90.8 to 94.7 %Copper (Cu)                           3.8 to 4.9 %Magnesium (Mg)                       1.2 to 1.8 %Manganese (Mn)                       0.3 to 0.9 %Iron (Fe)                                0 to 0.5 %Silicon (Si)                               0 to 0.5 %Zinc (Zn)                               0 to 0.25 %Zirconium (Zr)                            0 to 0.2 %Residuals                               0 to 0.15 %Titanium (Ti)                            0 to 0.15 %Chromium (Cr)                            0 to 0.1 %